Study on preparation and properties of expansive fireproof coatings containing different synergistic agents

Rong-rong Zheng1*, Lei Han1, Shu-wu Chen3, Hong-tao Wu3, Wei-xing Li2, Ji-xin Li1 and Haiyue Wang1

1School of Petrochemical Engineering, Shenyang University of Technology, Shenyang Liaoning 110870, China

2Liaoning Inspection, Testing and Certification Center, Shenyang Liaoning 110870, China

3Aromatics Laboratory, Liaoyang Petrochemical Company, Petrochina, Liaoyang Liaoning 110003, China

*Corresponding author: Rong-rong Zheng, School of Petrochemical Engineering, Shenyang University of Technology, Shenyang Liaoning 110870, China, E-mail: [email protected]

Received: July 29, 2022, Manuscript No. tsac-22-72539; Editor assigned: August 2, 2022, PreQC No. tsac-22-72539 (PQ); Reviewed: August 17, 2022, QC No. tsac-22-72539 (Q); Revised: August 22, 2022, Manuscript No. tsac-22-72539 (R); Published date: August 27, 2022. DOI: 10.37532/0974-7419.2022.22(8).209

Abstract

In this paper, the transition metal oxide (Ni2O3), 4A molecular sieve, sepiolite and montmorillonite were selected as the cooperative agent of the expansive flame retardant system and applied to the fire retardant coating. The study focuses on the influence of four coefficient agents on the fire resistance of the coating. The specific content is to compare the coefficient effect of metal oxide Ni2O3, 4 Å molecular sieve, sepiolite and montmorillonite through combustion back temperature test, and study the influence of four coefficient agents on the fire resistance of the coating. Co-effectors can significantly change the pyrolytic carbonization process of the inflatable flame retardant system and strengthen the fire resistance of the inflatable flame retardant coatings. Ni2O3, 4 Å molecular sieve, sepiolite and montmorillonite were added to the double cyclodragon phosphate expansive flame retardant epoxy coatings, respectively, and the effect of the coagent on the fire resistance of the coating was studied. The results of back temperature test show that the fire resistance time of APP/Ni2O3 and APP/4 Å coating films at 400℃ is 1025 s and 975 s, respectively, which is close to or even longer than that of APP/AE56 and APP/DK4 coating systems, respectively. However, the fire resistance of APP/Ni2O3 and EPAPP/4 Å coating films at low temperature is general. The fire resistance below 350℃ is short.

Retracted Note

Retracted: Study on Preparation and Properties of Expansive Fireproof Coatings Containing Different Synergistic Agents, had been accepted for publication in the Analytical chemistry: an Indian journal considering the statements provided in the article as the personal opinion of the author to be completely unbiased. The article was published solely on the basis of the opinion provided by the reviewers. But due to some unforeseen divergences between the author and the journal, the article is being retracted.

20+ Million Readerbase

Select your language of interest to view the total content in your interested language

Table of Contents

Google Scholar citation report
Citations : 688

Analytical Chemistry: An Indian Journal received 688 citations as per Google Scholar report

Indexed In

  • CASS
  • Google Scholar
  • Open J Gate
  • China National Knowledge Infrastructure (CNKI)
  • CiteFactor
  • Cosmos IF
  • Electronic Journals Library
  • Directory of Research Journal Indexing (DRJI)
  • Secret Search Engine Labs

Read More

Recommended Conferences

Flyer
Global Tech Summit