Fabrication and Characterization of Organic Light Emitting Diode Using FTO/Pentacene as Bilayer Anode

Author(s): Saikia D* and Sarma R

Pentacene films on FTO surface for affecting the hole injection probability in Organic Light Emitting Diode (OLED) has been investigated. Five kinds of organic light emitting diodes with tris (8-hydroxyquinoline) aluminium (Alq3) as emitting layers were fabricated. It was found that hole injection is directly affected by the different thickness of pentacene films on FTO surface. The OLED device with FTO/pentacene (6 nm) anode shows better device efficiency compared with bare FTO anode and that of other thickness of pentacene films. Enhanced device performance is due to the better surface morphology with large hole mobility, and highest figure of merit (FOM) value of FTO/pentacene (6 nm) bilayer anode combination. In this work N, N’-bis (3-methyl phenyl)-N, N’ (phenyl)-benzidine (TPD) used as hole transport layer and lithium fluoride (LiF) are used as electron injection layer. Our result suggests that the FTO/pentacene (6 nm) anode is an excellent choice to enhanced the hole injection in OLED devices. Here, we obtained maximum value of current and power efficiency are 6.6 Cd/A and 3.4 lm/W respectively.


Share this       

Share this Page

Table of Contents

Flyer