Fatigue Corrosion of 316lss Different Chromium Content

Author(s): D. Bubesh Kumar, K. G. Muthurajan

Fatigue corrosion of 316LSS having different chromium content, the fatigue corrosion was carried out in different chromium content 10% to 16% 316L stainless steel. The test was carried out in surface impact fatigue corrosion machine. The pitting life was calculated, it gives the fatigue corrosion resistance of 316LSS and S-N curve was plotted.